Product Details:
|
DGM: | Non-dangerous | Alloy Class: | Red Brass |
---|---|---|---|
Product Name: | Brass Faucet Desofin | Application: | De Oxidation Low Pressure Casting |
High Light: | Smooth Brass Faucet Desofin,Refiner Brass Faucet Desofin,Low Pressure Casting Grain Refiner |
Desofin Additive Pat Applied for B2 Alloy. What we can found the smooth surface.
The Better Ductility.
The Potential Savings:
1. Savings over the cost of purchasing fine grained ingot.
2. Energy savings resulting from lower casting temperature.
3. Materials savings. It's not necessary to refine foundry scrap. I.E gates, risers and turnings already grain refined.
Alloy Class and General Parameters |
Dosage |
Expected Results
|
Special Instructions |
||
Grain Refinement | Deoxy-dation | Reduced Casting Temp. | |||
Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb less than 0.5%.) |
150 grams per metric ton (5 grams per 100 lb.) |
YES |
YES |
YES |
Grain refinement occurs when copper content is between 57 and 63 percent. Optimal grain refinement occurs when copper content is 59.5 percent and aluminum content is 0.6 percent. See Notes 1 and 2. |
Leaded Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb more than 0.5%.) |
150 grams per metric ton (5 grams per 100 lb.) |
YES |
YES |
YES |
|
High Strength Yellow Brass (Manganese Bronze) (Over 17% Zn. Over 2% total Al, Mn. Sn, Ni, Fe. Si less than 0.5%. Pb less than 0.5%. Sn less than 6%) |
50 grams per metric ton (5 grams per 100 lb.) |
May reduce grain if Sn + Fe is less than 0.5% |
YES |
YES |
|
Red Brass (2% to 8% Zn. Sn less than Zn. Pb under 0.5%) |
200 grams per metric ton (9 grams per 100 lb.) |
NO |
YES |
YES |
Use without AL tubes. Add to transfer ladle along with phos copper. If high oxygen occurs, add Mn before adding DesofinTM. |
Aluminum Bronze (Al 5% to 15%. Fe up to 10% - with or without Mn or Ni. Si less than 0.5%) |
200 grams per metric ton (18 grams per 100 lb.) |
NO |
YES |
YES |
If high oxygen occurs, add Mn before adding DesofinTM. |
Tin Bronze (Sn 2% to 20%. Zn less than Sn. Pb under 0.5%) |
200 grams per metric ton (9 grams per 100 lb.) |
NO |
YES |
YES |
Use without Al tubes. Add to transfer ladle along with phos copper |
Notes: 1. If Sn + Fe is greater than 0.5%, intermetallic compounds will form that will leave "comet tails" when casting is polished. 2. Miller & Englehardt Co., lltd recommends use of "B-2" yellow brass alloy with DesofinTM for permanent molding applications. B[1]2 alloy composition: Cu 59.5 to 61.5%; Pb 0% to 3.0%; Al 0.5% to 0.7%, Ni 1%; Sn + Fe 0.5 % max, Mn 0.02% max, Si 0.02% max, Zn balance. |