Product Details:
|
| Product Name: | Desofin Additive | Application: | Brass Grain Fined |
|---|---|---|---|
| Usage: | Brass Ingot Melting | Dosage: | 5 Grams Per 100 Lb |
| Expected Results: | Grain Refinement | Brand: | Desofin |
| High Light: | Ingot Melting Brass Grain Refiner,Reduced Casting Temp Brass Grain Refiner,Desofin brass grain fined |
||
Desofin, the trademark chemical powder, would be used to the following alloys:
|
Alloy Class and General Parameters |
Dosage |
Expected Results
|
Special Instructions |
||
| Grain Refinement | Deoxy-dation | Reduced Casting Temp. | |||
| Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb less than 0.5%.) |
150 grams per metric ton (5 grams per 100 lb.) |
YES |
YES |
YES |
Grain refinement occurs when copper content is between 57 and 63 percent. Optimal grain refinement occurs when copper content is 59.5 percent and aluminum content is 0.6 percent. See Notes 1 and 2. |
| Leaded Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb more than 0.5%.) |
150 grams per metric ton (5 grams per 100 lb.) |
YES |
YES |
YES |
|
| High Strength Yellow Brass (Manganese Bronze) (Over 17% Zn. Over 2% total Al, Mn. Sn, Ni, Fe. Si less than 0.5%. Pb less than 0.5%. Sn less than 6%) |
50 grams per metric ton (5 grams per 100 lb.) |
May reduce grain if Sn + Fe is less than 0.5% |
YES |
YES |
|
|
Red Brass (2% to 8% Zn. Sn less than Zn. Pb under 0.5%) |
200 grams per metric ton (9 grams per 100 lb.) |
NO |
YES |
YES |
Use without AL tubes. Add to transfer ladle along with phos copper. If high oxygen occurs, add Mn before adding DesofinTM. |
|
Aluminum Bronze (Al 5% to 15%. Fe up to 10% - with or without Mn or Ni. Si less than 0.5%) |
200 grams per metric ton (18 grams per 100 lb.) |
NO |
YES |
YES |
If high oxygen occurs, add Mn before adding DesofinTM. |
|
Tin Bronze (Sn 2% to 20%. Zn less than Sn. Pb under 0.5%) |
200 grams per metric ton (9 grams per 100 lb.) |
NO |
YES |
YES |
Use without Al tubes. Add to transfer ladle along with phos copper |
| Notes: 1. If Sn + Fe is greater than 0.5%, intermetallic compounds will form that will leave "comet tails" when casting is polished. 2. Miller & Englehardt Co., lltd recommends use of "B-2" yellow brass alloy with DesofinTM for permanent molding applications. B[1]2 alloy composition: Cu 59.5 to 61.5%; Pb 0% to 3.0%; Al 0.5% to 0.7%, Ni 1%; Sn + Fe 0.5 % max, Mn 0.02% max, Si 0.02% max, Zn balance. | |||||
The following pictures show the performance after adding Desofin:
B2 Alloy of Cu59.5
Perfect grain refined cup