Home Products Graphite Mould

High Density Custom Graphite Mould For Gold 0.1% Ash Bending Strength Melting

All Products

Graphite Raw Material
(17)

Natural Flake Graphite
(64)

Graphite Petroleum Coke
(105)

Graphite Anode Material
(11)

Calcined Petroleum Coke
(39)

High Purity Graphite
(45)

Expandable Graphite Powder
(92)

Graphite Foil Roll
(14)

Spherical Graphite
(41)

Micronized Graphite Powder
(41)

Desofin
(12)

Graphite Release Agent
(9)

Graphite Mould
(4)

Amorphous Graphite Powder
(6)

Synthetic Graphite Powder
(9)

Carbon Raiser
(2)

Certification

I'm Online Chat Now

High Density Custom Graphite Mould For Gold 0.1% Ash Bending Strength Melting

Large Image : High Density Custom Graphite Mould For Gold 0.1% Ash Bending Strength Melting

Product Details:

Place of Origin:	Qingdao
Brand Name:	ME
Model Number:	as ordered

Payment & Shipping Terms:

Minimum Order Quantity:	10 sets
Packaging Details:	master carton as the ordered quantity
Delivery Time:	15 working days
Payment Terms:	T/T, L/C

Contact Now

High Density Custom Graphite Mould For Gold 0.1% Ash Bending Strength Melting

Description

Bulk Density:	1.9	Hardness:	50
Resistivity:	10	Bending Strength:	42
Compressive Strength:	86	Ash:	0.1%
Highlight:	High density Custom Graphite Mould , Custom Graphite Mould 0.1% Ash , 0.1% Ash graphite ingot mold

Technical data : 

Max Grain Size	Bulk Density g/cc	Specific Resistivity μΩ·m	Flexural Strength Mpa	Compressive Strength Mpa	Shore Hardness	C.T.E(100-600℃) ×10-6/℃
45µm	≥1.78	≤12.0	≥30.0	≥60.0	≥40.0	≤3.2
45µm	≥1.83	≤10.0	≥38.0	≥80.0	≥40.0	≤3.5
22µm	≥1.80	≤15.0	≥37.0	≥78.0	≥50.0	≤4.0
22µm	≥1.83	≤13.0	≥40.0	≥80.0	≥50.0	≤3.9

Graphite mould performance:

1.In high temperature in most of the copper base tire body sintering( temperature above 800 ºC) intensity increases with
temperature rise
2. Good lubrication and abrasion resistance.
3. Easy to process, good mechanical processing performance, can be made into a complex shape, high precision mold.